The Newcastle University research output collection, currently available on ePrints, will shortly be moving to a new open repository platform, Figshare. To prepare for the data migration we have paused adding new content to ePrints, and will resume once the new repository is launched. During this time you will continue to have access to ePrints (but no new content will appear). We will share updates here when available.

Vacuum consolidation of commingled thermoplastic matrix composites for marine applications

Lookup NU author(s): Muhammad Ijaz, Dr Peter Wright, Professor Geoff Gibson

Downloads

Full text for this publication is not currently held within this repository. Alternative links are provided below where available.

Abstract

An experimental and modelling study was conducted on the vacuum consolidation of commingled glass/thermoplastic composites as part of a larger project on manufacturing large monolithic structures from these precursors, such as those that could be used for marine structures. Two matrices were employed: semi-crystalline PET and an amorphous PET copolymer. Samples of commingled fabric were processed into consolidated composites by means of both a convective oven, as would be used in a real marine production environment, and a small scale experimental characterisation rig, designed to measure consolidation accurately. The samples were then cooled to room temperature. In this paper, the thermal and consolidation characterisation of these fabrics is reported. Thermally induced consolidation was observed to occur in two stages: a low temperature solid state de-bulking near to T-g, followed by full melt impregnation at a higher temperature. Both stages were modelled separately using an empirical model based on the Kamal equation. The measured consolidation vs. time profiles suggested a rapid impregnation and wetting of the fibres, occurring near to the melting point of the semi-crystalline polymer. The PET melting endotherm and crystallisation exotherm had little effect on the observed thermal profiles, suggesting that these effects could possibly be neglected when modelling the process.

Publication metadata

Author(s): Ijaz M, Wright PNH, Robinson M, Gibson AG

Publication type: Conference Proceedings (inc. Abstract)

Publication status: Published

Conference Name: International Conference on Advanced Marine Materials and Coatings

Year of Conference: 2006

Pages: 45-61

Publisher: Royal Institution of Naval Architects

Library holdings: Search Newcastle University Library for this item

ISBN: 9781905040223

Share